ALLOYS
  
 
 
Type Alloy- abbreviationa Suitability Chemical composition in % (m/m)
C Cr Ni Mn Mo W V Nb Others Balance
A Fe1 p 0,4 3,5 - 0,5 to 3 1 1 1 - - Fe
B Fe2 p 0,4 to 1,2 7 1 0,5 to 0,3 1 1 1 - - Fe
C Fe3 s t 0,2 to 0,5 1 to 8 5 3 4,5 10 1,5 - Co, Si Fe
D Fe4 s t (p) 0,2 to 1,5 2 to 6 4 3 10 19 4 - Co, Ti Fe
  Fe5 c p s t w 0,5 0,1 17 to 22 1 3 to 5 - - - Co, Al Fe
  Fe6 g p s 2,5 10 - 3 3 - - 10 Ti Fe
E Fe7 c p t 0,2 4 to 30 6 3 2 - 1 1 Si Fe
F Fe8 g p t 0,2 to 2 5 to 18 - 0,3 to 3 4,5 2 2 10 Si, Ti Fe
G Fe9 k (n) p 0,3 to 1,2 19 3 11 to 18 2 - 1 - Ti Fe
H Fe10 c k (n) p z 0,25 17 to 22 7 to 11 3 to 8 1,5 - - 1,5 Si Fe
I Fe11 c n z 0,3 18 to 31 8 to 20 3 4 - - 1,5 Cu Fe
J Fe12 c (n) z 0,08 17 to 26 9 to 26 0,5 to 3 4 - - 1,5 - Fe
  Fe13 g 1,5 6,5 4 0,5 to 3 - - - 1,5 B, Ti Fe
K Fe14 g 1,5 to 4,5 25 to 40 4 0,5 to 3 4 - - - - Fe
L Fe15 g 4,5 to 5,5 20 to 40 4 0,5 to 3 2 - - 10 B Fe
M Fe16 g z 4,5 to 7,5 10 to 40 - 3 9 8 10 10 B, Co Fe
  Fe20 c g t z Hardening Compon.b - - - - - - - - Fe
N Co1 c k t z 0,6 20 to 35 10 0,1 to 2 10 15 - 1 Fe Co
O Co2 t z (c s) 0,6 to 3 20 to 35 4 0,1 to 2 - 4 to 10 - - Fe Co
  Co3 t z (c s) 1 to 3 20 to 35 4 2 1 6 to 14 - - Fe Co
P Ni20 c g t z Hardening Compon.b - - - - - - - - Fe
Q Ni1 c p t 1 15 to 30 Rest 0,3 to 1 6 2 1 - Si, Fe, B Ni
R Ni2 c k p t z 0,1 15 to 30 Rest 1,5 28 8 1 4 Co, Si, Ti Fe
  Ni3 c p t 1 1 to 15 Rest 0,3 to 1 6 2 1 - Si, Fe, B Fe
  Ni4 c k p t z 0,1 1 to 15 Rest 1,5 28 8 1 4 Co, Si, Ti Fe
S Cu1 c (n) - - 6 15 - - - - Al, Fe, Sn Cu
  Al1 c n - - 10 to 35 0,5 - - - - Cu, Si Al
  Cr g n 1 to 5 Rest - 1 - - 15 to 30 - Fe, b, Si, Zv Cr
       
c: corrosion resistant, g: abrasion resistant, k: work-hardening, n: non magneticaly, p: impact resistant, s: cutting power resistant, t: heat resistant,
z: non-scaling, w: age-artifically, ( ) perhaps not suitable forall alloys in this list
a: Alloys not mentioned in this table should be marked "similar" with the prefix "Z"
* Alloy marks and chemical composition according DIN EN 14700
** Alloy Group as per old DIN 8555-1